Summary: According to the National Recommended Standard GB / T 13519-2016, herein polyethylene shrink film with a friction coefficient of the sample, Labthink MXD-02 friction coefficient tester detects an enterprise production and testing process, device parameters, scope and The test principle and other contents are introduced to provide reference for enterprises to strengthen the friction coefficient performance test and quality monitoring of polyethylene shrink film.
Key words: friction coefficient, polyethylene, shrink film, friction coefficient meter, GB/T 13519-2016 , static friction coefficient, dynamic friction coefficient
1 , meaning
The friction coefficient is an important factor affecting the ease of use of materials. The phenomenon of slippage, deviation, and poor opening during the use of packaging materials are all related to the improper friction coefficient. Polyethylene shrink film is a common heat shrink film material, which is commonly used in the packaging of beer, beverage, wood, ceramics, electronic products, industrial finished products, etc. If the friction of polyethylene shrink film is low, and the above products The slidability is large and the product is prone to falling off. The national standard GB/T 13519-1992 of polyethylene shrink film has been rejected . The coefficient of friction is not covered in the polyethylene heat shrinkable film, and its replacement standard GB/T 13519-2016 "polyethylene heat shrinkable film for packaging" ( 2016) in implementation of resolution 1 November) will be included in the coefficient of friction polyethylene shrink film other content inspection performance, the standard has not yet made specific requirements on the friction coefficient index, only the provisions negotiated by both parties, but polyethylene shrink The film puts forward higher requirements. Therefore, the detection and control of the friction coefficient of polyethylene shrink film is an effective way to improve its performance, and it is also the basic requirement of the standard.
2 , testing basis
GB/T 13519-2016 specifies the friction coefficient according to the requirements of GB 10006-1988 "Method for determination of friction coefficient of plastic film and sheet". GB10006 is suitable for non-stick plastic film and sheet with thickness less than 0.2mm on the surface of itself or other materials. Test of static friction coefficient and dynamic friction coefficient when sliding.
3 , test samples
The sample tested in this test is a polyethylene shrink film produced by a company, and the coefficient of friction between the test sample and the glass.
4 , testing equipment
In this paper, the friction coefficient of the sample is tested by MXD-02 friction coefficient meter. The equipment is independently developed and produced by Jinan Languang Electromechanical Technology Co., Ltd.
Figure 1 MXD-02 friction coefficient meter
4.1 Test principle
The friction coefficient is the ratio of the friction between the two contact surfaces and the vertical force acting on one of the surfaces. In this test, the test sample is set to the test speed and the friction surface by applying a certain pressure to the sample. The coefficient of friction of the sample is obtained by the value of the tensile force at the time of relative sliding.
4.2 Scope of application
(1) This equipment is specially used to measure plastic film and sheet, rubber, paper, cardboard, woven bag, textile, non-woven fabric, metal composite tape for communication cable, conveyor belt, wood, coating, brake pad, wiper Static friction coefficient and dynamic friction coefficient when materials such as shoe materials and tires slide. It can also be used for the determination of the slipperiness of daily necessities such as cosmetics and eye drops.
(2) This equipment can meet many national and international standards such as GB 10006 , ISO 8295 , ASTM D1894 , TAPPI T816 .
4.3 Test parameters
The equipment can simultaneously measure the dynamic and static friction coefficient of the sample in one test; the test load range is 0 ~ 5 N , and the test accuracy is 0.5 grade; according to the different test standards, the equipment has 70 mm and 150 mm tests. The stroke is available for selection; the standard slider quality used in the equipment is 200 g . The sliders of other weights can be customized according to specific needs; the instrument test bench and test slider are demagnetized and residual magnetic detection, which effectively reduces system test error. .
5 , the test process
(1) Cut 3 pieces of 8 cm × 20 cm sample from the polyethylene shrink film sample to be tested , and use the inner surface of the sample as the test surface. When cutting the sample, the inner surface should not be touched by hand to ensure that the inner surface is not Scratched and contaminated.
(2) Fix one of the samples on the slider, the outer surface is in direct contact with the slider, and the glass plate for friction is fixed on the steel plate of the device. During the process of fixing the sample and the glass plate, the friction zone cannot be touched by hand.
(3) Place the slider without impact on the middle of the glass plate to ensure that the force measurement system is not affected.
(4) Set test parameters such as test speed and test stroke. Click the Start Test option and the test starts.
(5) After the sample was in contact with the glass plate for 15 s , the relative movement began. The device automatically records changes in force values ​​during the test and calculates test results.
(6) Repeat the loading process - click the test process to test the dynamic and static friction coefficients of the remaining two samples.
6 , test results
The friction coefficient of the polyethylene shrink film sample was taken as the arithmetic mean of the test results of three samples, the static friction coefficient was 0.131 , and the dynamic friction coefficient was 0.097 .
7 , conclusion
The friction coefficient is an important factor affecting the packaging effect and performance of polyethylene shrink film, and the new GB/T 13519-2016 increases the detection requirement for the friction coefficient of polyethylene shrink film. From the test process of the friction coefficient between the polyethylene shrink film sample and the glass plate, the test is simple, the equipment is easy to operate, and the friction coefficient of the polyethylene shrink film can be accurately reflected. The friction surface selected is different, and the friction coefficient measured by the same sample is different. Therefore, when testing the friction coefficient of the polyethylene shrink film, the friction surface should be reasonably selected according to the contact product. In addition, the sample friction area should be prevented from being contaminated during the sample preparation process to ensure the accuracy of the test results. Jinan Languang Electromechanical Technology Co., Ltd. is a high-tech enterprise specializing in R&D, production and packaging inspection services for packaging inspection equipment. It covers a wide range of performances including barrier performance, physical and mechanical properties, and hygienic performance . The more you understand, the more you trust! Labthink is looking forward to enhancing technical communication and cooperation with enterprises and institutions in the industry!
Lithium Tert-butoxide Basic Information
Product Name: Lithium tert-butoxideCAS: 1907-33-1
MF: C4H9LiO
MW: 80.05
EINECS: 217-611-5
Mol File: 1907-33-1.mol
Lithium tert-butoxide Chemical Properties
Boiling point: 68-70 °C
Density: 0.89 g/mL at 20 °C
Fp: −2 °F
Storage temp: Flammables area
Solubility: Soluble in toluene, hexane, tetrahydrofuran and methyl tert-butyl ether.
Form: Liquid
Color: Brown
Specific Gravity: 0.89
Sensitive: Moisture Sensitive
Lithium Tert-Butoxide,Potassium Tert-Butoxide,Sodium Tert-Butoxide,Potassium Methoxide,Sodium Methoxide,Lithium Methoxide
Shandong YingLang Chemical Co.,Ltd , https://www.sdylhgtrade.com